RDX在2,4-二硝基苯甲醚(DNAN)低共熔体系中的溶解度
作者:
作者单位:

中国工程物理研究院化工材料研究所,中国工程物理研究院化工材料研究所,中国工程物理研究院化工材料研究所,北京理工大学理学院化学系,中国工程物理研究院化工材料研究所,中国工程物理研究院化工材料研究所

作者简介:

罗观(1972－)，男，硕士，主要从事含能材料配方及装药技术研究。

通讯作者:

基金项目:

中国工程物理研究院科学技术发展基金(2009B0302031)


Solubility of RDX in melt DNAN/MNA
Author:
Affiliation:

Institution of Chemical Materials,China Academy of Engineering Physics,Institution of Chemical Materials,China Academy of Engineering Physics,Institution of Chemical Materials,China Academy of Engineering Physics,Physical Chemistry,School of Science,Beijing Institute of Technology,,Institution of Chemical Materials,China Academy of Engineering Physics,Institution of Chemical Materials,China Academy of Engineering Physics

Fund Project:

  • 摘要
    • |
  • 图/表
    • |
  • 访问统计
    • |
  • 参考文献
    • |
  • 相似文献
    • |
  • 引证文献
    • |
  • 资源附件
    摘要:

    采用液相色谱法，在87~95.3 ℃温度范围内，测定了RDX在2, 4-二硝基苯甲醚(DNAN)与N-甲基-4-硝基苯胺(MNA)低共熔体系中的溶解度。优化了色谱分离条件:流动相甲醇/水=6/4(V/V)，流速为1.0 mL·min-1；检测波长254 nm，进样量5.0 μL。实验考察了不同粒径的RDX、平衡时间以及温度对溶解度的影响，在低共熔物体系DNAN/MNA中，建立了RDX溶解度-温度关系曲线。结果表明，RDX在共熔体系中溶解度范围为9.39~10.28 g，并随着体系温度的升高而增大。

    Abstract:

    High performance liquid chromatography (HPLC) was employed to analysis the solubility of RDX in melting DNAN/MNA at the range of 87 ℃ to 95.3 ℃. The optimal chromatography conditions were as following: mobile phase is methanol/water=6/4 (V/V), and flow rate 1.0 mL·min-1, and wavelength of detector 254 nm, and injection volume 5.0 μL. The influence of particle size, equilibration time and temperature programming on solubility was studied. Under the optimum condition, the curve of the solubility of RDX in DNAN/MNA as a function of temperature was built. Results show that the solubility of RDX increases with increasing of the temperature.

    参考文献
    相似文献
    引证文献
文章指标
  • PDF下载次数:
  • HTML阅读次数:
  • 摘要点击次数:
  • 引用次数:
引用本文

罗观,黄辉,王平胜,等. RDX在2,4-二硝基苯甲醚(DNAN)低共熔体系中的溶解度[J].含能材料, 2012, 20(4):437-440. DOI:10.3969/j. issn.1006-9941.2012.04.012.
Luo guan, huang hui, wang ping-sheng, et al. Solubility of RDX in melt DNAN/MNA[J]. Chinese Journal of Energetic Materials, 2012, 20(4):437-440. DOI:10.3969/j. issn.1006-9941.2012.04.012.

复制
历史
  • 收稿日期: 2011-08-18
  • 最后修改日期: 2012-05-18
  • 录用日期: 2012-03-22
  • 在线发布日期: 2012-07-26
  • 出版日期:

技术支持:北京勤云科技发展有限公司 ICP:蜀ICP备10207813号-5

今日访问量： 总访问量：