常温和75 ℃条件下PBX-2炸药射弹撞击响应特性
Response Characteristic of PBX-2 Explosive under Projectile Impact at Ambient Temperature and 75 ℃
  • 摘要
  •  
  • 参考文献
  •  
  • 引证文献
  •  
  • 相似文献
中文摘要:
      为了研究常温和75 ℃条件下PBX-2炸药射弹撞击响应特性,采用高温撞击试验装置对PBX-2炸药进行了射弹撞击试验。采用冲击波超压传感器测量了炸药的反应超压,结合回收样品综合分析了常温和75 ℃下炸药的响应特性。采用有限元程序LS-DYNA计算分析了不同撞击速度对应的常温和75 ℃ PBX-2炸药的受力变化。结果表明,常温下PBX-2炸药撞击点火反应速度阈值为263.5~269.9 m·s-1; 加热至75 ℃时,PBX-2炸药撞击点火反应速度阈值为316~367 m·s-1。相比常温状态,当射弹撞击速度低于800 m·s-1时, 75 ℃条件下PBX-2炸药反应程度明显下降,但射弹撞击速度高于800 m·s-1时,约1.54 GPa的输入压力就能使75 ℃ PBX-2炸药产生剧烈反应。
中文关键词: 撞击安全性  高聚物粘结炸药(PBX)  响应特性
英文摘要:
      To investigate the response characteristic of PBX-2 explosive under projectile impact at ambient temperature and 75 ℃, the projectile impact tests of PBX-2 explosive were conducted by a high temperature impact test device. The reaction overpressure of the explosive was measured by the shock-wave overpressure sensor and the response characteristics of the explosive at ambient temperature and 75 ℃ were comprehensively analyzed using recovered samples. The stress variation of PBX-2 at ambient temperature and 75 ℃ at different impact velocities was calculated and analyzed using finite element program LS-DYNA. The results show that the threshold velocity of ignition reaction for PBX-2 explosive at ambient temperature is from 263.5 m·s-1 to 269.9 m·s-1, while the threshold velocity of ignition reaction for PBX-2 heated to 75 ℃ is from 316 m·s-1 to 367 m·s-1. Compared with ambient temperature state, when the projectile velocity is less than 800 m·s-1, the reaction degree of PBX-2 at 75 ℃ obviously decreases. However, when the projectile velocity is higher than 800 m·s-1, the impact pressure of about 1.54 GPa can make the PBX-2 at 75 ℃ occur violent reaction.
英文关键词: impact safety  polymer bonded explosive (PBX)  reaction characteristic
DOI:10.11943/j.issn.1006-9941.2017.08.011
基金项目:国家自然科学基金(11472051),中国工程物理研究院化工材料研究所科技创新基金(KJCX-201503)
引用文献:代晓淦,于劭钧,黄风雷,文玉史,郑雪,姚奎光.常温和75 ℃条件下PBX-2炸药射弹撞击响应特性[J].含能材料,2017,25(8):683~688
作者单位E-mail
代晓淦 中国工程物理研究院化工材料研究所, 四川 绵阳 621999 zhangy2005767@sina.com,yaokuiguang1987@163.com 
于劭钧 中国工程物理研究院化工材料研究所, 四川 绵阳 621999  
黄风雷 北京理工大学机电学院, 北京 100081  
文玉史 中国工程物理研究院化工材料研究所, 四川 绵阳 621999  
郑雪 中国工程物理研究院化工材料研究所, 四川 绵阳 621999  
姚奎光 中国工程物理研究院化工材料研究所, 四川 绵阳 621999 yaokuiguang1987@163.com 
摘要点击次数: 287
全文下载次数: 298
HTML 查看全文   查看/发表评论   下载PDF阅读器

更多>>

更多>>

分享按钮