Al/PTFE活性材料的动态力学行为和撞击点火特性
Dynamic Mechanical Behavior and Impact Ignition Characteristics of Al/PTFE Reactive Materials
  • 摘要
  •  
  • 参考文献
  •  
  • 引证文献
中文摘要:
      为探究铝/聚四氟乙烯(Al/PTFE)活性材料在动态载荷下的力学行为及其点火机理,采用分离式霍普金森压杆对不同成型压力下所制备的Al/PTFE试件进行动态压缩试验。试验结果显示,当应变率为2960~5150 s-1时,Al/PTFE试件在动态加载下呈现出典型的弹塑性力学行为,成型压力为50~150 MPa时,Al/PTFE试件的屈服强度和硬化模量并未表现出应变率效应。成型压力30~80 MPa时,Al/PTFE试件的速度点火阈值随成型压力的增加从28.77 m·s-1缓慢升高到29.22 m·s-1,材料的点火延迟时间始终保持在600~700 μs。当成型压力达100 MPa时,Al/PTFE试件的速度点火阈值大幅下降至26.60 m·s-1,且随着撞击速度的提高,活性材料的点火延迟时间由1000~1100 μs降到600~700 μs。结合扫描电镜结果可知,成型压力为100~150 MPa时,活性材料内部的局部大尺寸孔洞是材料速度点火阈值下降的重要因素。Al/PTFE活性材料的撞击引发点火特性主要与外部载荷和内部微观形貌有关。
中文关键词: 铝/聚四氟乙烯(Al/PTFE)活性材料  力学行为  速度点火阈值  点火延迟时间  点火机理
英文摘要:
      In order to investigate the dynamic behavior and ignition mechanism of Al/polytetrafluoroethylene(PTFE) reactive material under dynamic loading, a Split Hopkinson Pressure Bar (SHPB) was used to conduct the dynamic compression experiment on reactive materials with different molding pressure. Experimental results show that the Al/PTFE reactive material exhibits typical elastic-plastic mechanical behavior under dynamic loading at strain rate ranging from 2960 s-1 to 5150 s-1. The yield strength and hardening modulus of Al/PTFE reactive materials do not show strain rate effect when the molding pressure is 50-150 MPa. The velocity ignition threshold increases slowly from 28.77 m·s-1 to 29.22 m·s-1 with the molding pressure. When the molding pressure increases to 100 MPa, the velocity ignition threshold drops significantly to 26.60 m·s-1. With the increase of the impact velocity, the ignition delay time for reactive materials with the molding pressure of 100-150 MPa decreases from 1000-1100 μs to 600-700 μs, while that of reactive materials with the molding pressure of 30-80 MPa maintains at 600-700 μs. Combining with results of Scanning Electron Microscopy, it is found that the local larger pores inside the reactive materials with higher molding pressure is the main factor for the sudden drop of the velocity ignition threshold. Therefore, the impact ignition characteristics of Al/PTFE reactive materials are mainly related to the external loading form and the internal micro-morphology.
英文关键词: Al/polytetrafluoroethylene(PTFE) reactive material  mechanical behavior  velocity ignition threshold  ignition delay time  ignition mechanism
DOI:10.11943/CJEM2019024
投稿日期:2019-01-24
最后修改日期:2019-07-08
网络出版日期:2019-07-05
书版出版日期:2020-01-21
基金项目:国家自然科学基金 11872124;爆炸科学与技术国家重点实验室课题(YBKT19-11)国家自然科学基金(11872124);爆炸科学与技术国家重点实验室课题(YBKT19-11)
引用文献:李尉,任会兰,宁建国,等.Al/PTFE活性材料的动态力学行为和撞击点火特性[J].含能材料,2020,28(1):38-45
作者单位E-mail
李尉 北京理工大学 爆炸科学与技术国家重点实验室 北京 100081 wesley@bit.edu.cn 
任会兰 北京理工大学 爆炸科学与技术国家重点实验室 北京 100081 huilanren@bit.edu.cn 
宁建国 北京理工大学 爆炸科学与技术国家重点实验室 北京 100081  
刘元斌 北京理工大学 爆炸科学与技术国家重点实验室 北京 100081  
摘要点击次数: 841
全文下载次数: 292
HTML  查看全文   查看/发表评论   下载PDF阅读器
附件

更多>>

更多>>

分享按钮