热老化对TATB基高聚物粘结炸药力学性能的影响
Effects of Thermal Ageing on Mechanical Properties of PBX Based on TATB
  • 摘要
  •  
  • 参考文献
  •  
  • 引证文献
中文摘要:
      对某TATB基高聚粘结炸药(PBX)进行了55~75 ℃加速老化试验,并对老化前后的样品进行了不同温度下压缩性能、拉伸性能和弯曲蠕变实验,用扫描电子显微镜对老化前后炸药高温拉伸断口形貌进行了观察。结果表明: 长期高温贮存后,TATB基高聚物粘结炸药晶体与粘合剂仍具有良好的粘合界面,其模量、破坏强度、破坏应变和稳态蠕变速率等力学性能指标均未发生明显的变化。
中文关键词: 材料科学  高聚物粘结炸药(PBX)  加速老化  力学性能
英文摘要:
      The accelerated thermal aging tests of PBX based on TATB were carried out by using a hot air oven from 55 ℃ to 75 ℃. The mechanical properties such as tensile strength, elongation at failure and modulus were measured before and after aging. Morphology of rapture section from tensile test at 55 ℃ was observed by using scanning electric microscopy (SEM). Results show that the mechanical properties and the interfacial mechanism between binder and TATB crystal do not undergo changes significant during the aging period.
英文关键词: materials science  polymer bonded explosive (PBX)  accelerated aging  mechanical property
DOI:10.3969/j.issn.1006-9941.2010.02.008
投稿日期:2009-07-02
最后修改日期:2009-09-25
网络出版日期:2010-04-16
基金项目:武器装备预先研究项目(42604020401)
引用文献:韦兴文,李敬明,涂小珍,等.热老化对TATB基高聚物粘结炸药力学性能的影响[J].含能材料,2010,18(2):157~161.WEI Xing-wen,LI Jing-ming,TU Xiao-zhen,et al. Effects of Thermal Ageing on Mechanical Properties of PBX Based on TATB[J]. Chinese Journal of Energetic Materials(Hanneng Cailiao),2010,18(2):157-161.
作者单位E-mail
韦兴文 中国工程物理研究院化工材料研究所, 四川 绵阳 621900 wei_xw@sina.com 
李敬明 中国工程物理研究院化工材料研究所, 四川 绵阳 621900  
涂小珍 中国工程物理研究院化工材料研究所, 四川 绵阳 621900  
王培 中国工程物理研究院化工材料研究所, 四川 绵阳 621900  
周筱雨 中国工程物理研究院化工材料研究所, 四川 绵阳 621900  
摘要点击次数: 2447
全文下载次数: 2590
HTML  查看全文   查看/发表评论   下载PDF阅读器

更多>>

更多>>

分享按钮