HNS的细化工艺研究
Study on the Preparation Technology of Ultrafine HNS
  • 摘要
  •  
  • 参考文献
  •  
  • 引证文献
中文摘要:
      研究了低温结晶法制备超细六硝基茋(HNS)的工艺,把炸药溶液高度分散成细流状态加到低温水中,并加入合适的表面活性剂,得到比表面积达23 m2·g-1,平均粒径为0.36 μm,纯度为98.5%的亚微米HNS。
中文关键词: 六硝基茋(HNS)  比表面积  颗粒度
英文摘要:
      The preparation technology of ultrafine hexanitrostilbene (HNS) by recrystallization method was presented. The high-dispersed explosive solution was splashed into low-temperature water and the fitting surfactant was added at the same time. Ultrafine HNS was obtained with specific surface area 23.00 m2·g-1, mean diameter 0.365 μm and purity 98.5%.
英文关键词: hexanitrostilbene (HNS)  specific surface area  particle size
投稿日期:2001-06-08
网络出版日期:2011-11-03
基金项目:国防科技预研项目(编号:42101030303)
引用文献:王平,秦德新,聂福德,等.HNS的细化工艺研究[J].含能材料,2001,9(4):153~155.WANG Ping,QIN De-xin,NIE Fu-de,et al. Study on the Preparation Technology of Ultrafine HNS[J]. Chinese Journal of Energetic Materials(Hanneng Cailiao),2001,9(4):153-155.
作者单位
王平 中国工程物理研究院化工材料研究所 四川 绵阳 621900 
秦德新 中国工程物理研究院化工材料研究所 四川 绵阳 621900 
聂福德 中国工程物理研究院化工材料研究所 四川 绵阳 621900 
陈娅 中国工程物理研究院化工材料研究所 四川 绵阳 621900 
辛芳 中国工程物理研究院化工材料研究所 四川 绵阳 621900 
梁叶明 中国工程物理研究院化工材料研究所 四川 绵阳 621900 
刘春 中国工程物理研究院化工材料研究所 四川 绵阳 621900 
摘要点击次数: 2252
全文下载次数: 1923
HTML  查看全文   查看/发表评论   下载PDF阅读器

更多>>

更多>>

分享按钮