高纯纳米HNS的制备与表征
Preparation and Characterization of High Purity Nano HNS
  • 摘要
  •  
  • 参考文献
  •  
  • 引证文献
中文摘要:
      采用溶液急冷重结晶和溶剂非溶剂重结晶相结合的方法得到了2,2′,4,4′,6,6′-六硝基茋(HNS) 高纯纳米颗粒。经过纳米化后,HNS的颗粒形貌更为圆滑,粒度分布处于58.9~231.6 nm之间,纯度由90.1%提高到99.44%,比表面积为19.27 m2·g-1。撞击感度测试表明,纳米HNS的撞击感度较之原料HNS有所降低,冲击片感度提高。
中文关键词: 有机化学  纳米炸药  2,2′,4,4′,6,6′-六硝基茋(HNS)  高纯度  溶剂反溶剂法
英文摘要:
      High purity nano HNS was prepared by the combination of solution quench recrystallization and solvent-antisolvent recrystallization. Results show that crystal appearance of nano HNS is smoother with particle size from 58.9 nm to 231.6 nm, and its purity is increased from 90.1% to 99.44%, the BET specific surface area is determined to be 19.27 m2·g-1. Sensitivity tests for the raw HNS and nano HNS indicate that nano HNS is less sensitive to impact than raw HNS, but more sensitive to short impulse shock waves.
英文关键词: organic chemistry  nano explosive  2,2′,4,4′,6,6′-hexanitro-stilbene (HNS)  high purity  solvent-antisolvent recrystallization
投稿日期:2007-09-28
网络出版日期:2011-05-06
引用文献:王晶禹,黄浩,王培勇,等.高纯纳米HNS的制备与表征[J].含能材料,2008,16(3):258~261.WANG Jing-yu,HUANG Hao,WANG Pei-yong,et al. Preparation and Characterization of High Purity Nano HNS[J]. Chinese Journal of Energetic Materials(Hanneng Cailiao),2008,16(3):258-261.
作者单位
王晶禹 中北大学国防重点学科实验室 山西 太原 030051 
黄浩 中北大学国防重点学科实验室 山西 太原 030051 
王培勇 中北大学国防重点学科实验室 山西 太原 030051 
陈健 中北大学国防重点学科实验室 山西 太原 030051 
刘红妮 西安近代化学研究所四部 陕西 西安 710065 
摘要点击次数: 2211
全文下载次数: 1972
HTML  查看全文   查看/发表评论   下载PDF阅读器

更多>>

更多>>

分享按钮