六硝基六氮杂异伍兹烷包覆钝感的探索
Investigation of Coating-desensitization of Hexanitrohexaazaisowurtzitane(HNIW)
  • 摘要
  •  
  • 参考文献
  •  
  • 引证文献
中文摘要:
      采用挤出造粒法、溶液悬浮法、水悬浮法三种不同的工艺,选用不同的包覆材料,如氟橡胶和丁腈橡胶,对ε-HNIW进行了包覆,并对包覆样品进行了扫描电镜分析和机械撞击感度测试,考察了其钝感效果及包覆工艺对样品机械撞击感度的影响。通过比较,溶液悬浮法、水悬浮法工艺制备的样品机械撞击感度要比挤出造粒法的低。在所选材料中,氟橡胶F-5作为粘结剂,采用水悬浮法工艺制备得到的以HNIW为基的混合炸药的机械撞击感度最低,特性落高值为42.5 cm。
中文关键词: 物理化学; 六硝基六氮杂异伍兹烷(HNIW,CL-20)  钝感  包覆  机械撞击感度
英文摘要:
      The ε-HNIW was coated by several kinds of materials such as fluororubber and chemigum by means of extruding-prilling,solution suspension and water suspension methods. The coated HNIW samples were evaluated by means of SEM and impact sensitivity test in order to confirm the desensitization effect and the effectiveness of the coating methods mentioned above. Results show that the solution suspension method is better than the extruding-prilling method to desensitization of HNIW. Among coated samples,impact sensitivity of ε-HNIW coated by fluororubber F-5 by water suspension method is the lowest,value of characteristic height(H50) is 42.5 cm.
英文关键词: physical-chemistry  hexanitrohexaazaisowurtzitane(HNIW)  coating  desensitization  impact sensitivity
投稿日期:2003-12-15
网络出版日期:2011-11-03
基金项目:总装跨行业预研基金项目(00J12.6.6.BQ0127)
引用文献:金韶华,于昭兴,欧育湘,等.六硝基六氮杂异伍兹烷包覆钝感的探索[J].含能材料,2004,12(3):147~150.JIN Shao-hua,YU Zao-xing,OU Yu-xiang,et al. Investigation of Coating-desensitization of Hexanitrohexaazaisowurtzitane(HNIW)[J]. Chinese Journal of Energetic Materials(Hanneng Cailiao),2004,12(3):147-150.
作者单位
金韶华 北京理工大学材料科学与工程学院 北京 100081 
于昭兴 北京理工大学材料科学与工程学院 北京 100081 
欧育湘 北京理工大学材料科学与工程学院 北京 100081 
陈树森 北京理工大学材料科学与工程学院 北京 100081 
松全才 北京理工大学材料科学与工程学院 北京 100081 
摘要点击次数: 1776
全文下载次数: 1542
HTML  查看全文   查看/发表评论   下载PDF阅读器

更多>>

更多>>

分享按钮