TATB颗粒温压成形PBX的初始细观损伤
作者:
作者单位:

(中国工程物理研究院化工材料研究所, 四川 绵阳 621999)

作者简介:

张伟斌(1972-),男,研究员,主要方向为先进材料检测与无损评价、CT应用技术研究、凝聚态物理。e-mail: weibinzhang1@163.com

通讯作者:

基金项目:

国家自然科学基金NSAF重点基金(U1330202)、国家自然科学基金青年基金(11204279)


Initial Mesoscopic Damage of TATB based PBX Pressed by Warm Compaction
Author:
Affiliation:

(Institute of Chemical Materials, China Academy of Engineering Physics, Mianyang 621999, China)

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
    摘要:

    用X射线微层析成像(X-μCT)技术无损研究了TATB造型颗粒经单、双向钢模温压(UWDC和BWDC)法和软模温等静压(IWSC)法成形的高聚物粘结炸药(PBX)三维微细结构特征。结果表明, 单向、双向压法压成的PBX内部存在初始细小裂纹和一些残余孔隙。初始损伤尺度范围从百微米至毫米。在相同温度(85 ℃)和压力(90 MPa)下, UWDC和BWDC法可产生初始细观损伤, 但IWSC法能避免初始细观损伤。

    Abstract:

    Three-dimension (3D) mesoscopic structure features of polymer bonded explosives (PBXs) pressed by unidirectional and bidirectional warm die compaction (UWDC and BWDC) and isostatic warm soft compaction (IWSC) methods with the modeling granules of TATB were nondestructively studied by X-ray micro-tomography (X-μCT) technique. Results show that the initial fine crack and some residual pores are existed in the PBXs pressed by unidirectional and bidirectional compaction methods. The scale range of initial mesoscopic damage is from hundred microns to millimeter. At the same temperature (85 ℃)and pressure (90 MPa), the initial mesoscopic damage can be produced by UWDC and BWDC methods, but this damage can avoid by IWSC method.

    参考文献
    相似文献
    引证文献
文章指标
  • PDF下载次数:
  • HTML阅读次数:
  • 摘要点击次数:
  • 引用次数:
引用本文

张伟斌,李敬明,杨雪海,等. TATB颗粒温压成形PBX的初始细观损伤[J].含能材料, 2015, 23(2):202-204. DOI:10.11943/j. issn.1006-9941.2015.02.018.
ZHANG Wei-bin, LI Jing-ming, YANG Xue-hai, et al. Initial Mesoscopic Damage of TATB based PBX Pressed by Warm Compaction[J]. Chinese Journal of Energetic Materials, 2015, 23(2):202-204. DOI:10.11943/j. issn.1006-9941.2015.02.018.

复制
历史
  • 收稿日期: 2014-05-26
  • 最后修改日期: 2014-06-18
  • 录用日期: 2014-06-23
  • 在线发布日期: 2015-02-09
  • 出版日期: 2015-02-12